An electron microscopy study of tweed microstructures and premartensitic effects in high damping 53Cu45Mn2A1 alloy
The evolution of tweed microstructure upon aging a 53Cu45Mn2Al alloy was studied in the transmission electron microscope (TEM). Characteristic (110) tweed contrast develops after the alloy is aged for 4 hours or longer at 400 C, which apparently is just within the miscibility gap, and is then cooled...