The variation of subgrain misorientation in aluminum with large steady-state creep strain
High purity aluminum was torsionally deformed to various strains up to 16.33 at a temperature of 644 K in this study. The variation in the dislocation substructure was determined with increasing strain. Recent work revealed that both the subgrain size and density of dislocations not associated with...