The effect of lattice defects on internal friction of niobium
Irradiation, cold-worked and quenching effects in arc melted commercial niobium have been studied using the low frequency (1 c/s) internal friction technique. A relaxation peak at about 110°K has been found after irradiation and cold-work, which is thought to involve the relaxation of disloc...