The influence of recrystallization on hot ductility
The deformation and fracture behaviour of polycrystalline copper matrix with and without silica particles was investigated by testing at tensile strain rates of 0.0004 s-1 and 0.004 s-1 over the temperature range of 250-900 °c and by examining the fractured specimens by light and electron microscopy...