Oxidation and wear behaviour of a work roll grade high speed steel
The oxidation behaviour of high speed steel (1.55 % C, 7.70 % Cr, 4.90 %V, and 2.00% Mo) was studied isothermally at 550 and 615'C for three different environmental conditions, two of which consisted in a mixture of dry air and water vapour flowing at a rate of 0.45 or 1.45 cm'/min respect...