The relationship between microstructure and wear rate in polycrystalline aluminas
A range of dense polycrystalline liquid phase aluminas was prepared by hot-pressing . and pressureless sintering methods with calcium silicate additions of 0.5, I, 5 and 10% by weight. The CaO:Si02 ratio varied betWeen 1:10 and 10:1. The microstructures wer~ systematically studied using analytical s...