Surface residual stress effects on stress corrosion cracking/hydrogen embrittlement behavior of AISI 4340 steel
A series of experiments was performed in an attempt to measure the effects of surface residual stresses on the stress corrosion cracking/hydrogen embrittlement (SCC/HE) behavior of AISI 4340 steel. Stress corrosion tests were performed under load control on cylindrical and notched tensile specimens...