Microyielding and flow in niobium alloy crystals
Oriented single crystals of niobium and dilute alloys with molybdenum and tantalum were deformed in tension between 77°K and 500°K, and the macroflow and slip parameters established. At high temperatures the main effect of alloying was to increase the flow stress, considerably more with molybdenum t...