Stress corrosion cracking of rotor steels in carbonate/bicarbonate and sodium hydroxide solutions
In this study, the stress corrosion behavior of 3.5%NiCrMoV and 1%CrMoV steels was investigated. Tests were conducted at 95°C in carbonate/bicarbonate and sodium hydroxide solutions. Results from slow strain rate tensile tests and fracture mechanics experiments were compared. A new, easily machinabl...