Effect of Different solidification rate on the high-temperature behavior of PWA1422 Nibased superalloy
碩士 === 義守大學 === 材料科學與工程學系 === 105 === In this study, MAR-M200 + Hf nickel-based superalloy was used Polycrystalline and superalloy with withdraw rate of DS 60mm/hr、120mm/hr、180mm/hr.Standard heat treatment procedures are solution treatment at 1200 ℃ for 4hr / ArC, the first aging at 1100 ℃ for 4hr /...