The interaction between dislocations and the spinodal nanostructure in a 2205 duplex stainless steel
碩士 === 國立臺灣大學 === 材料科學與工程學研究所 === 103 === A 2205 duplex stainless steel is susceptible to severe embrittlement after aging at 475ºC. Microstructures of the unaged and aged specimens (heat-treated at 475ºC for 64h) were investigated by different deformation tests, in order to elucidate the cause...