Phase Transformation Analysis and Fracture Morphology Observation of 304 Stainless Steel Wire after Cold Drawing and Annealing Treatments
碩士 === 逢甲大學 === 纖維與複合材料學系 === 102 === In this study, the diameter 1.0 mm of 304 stainless steel wires were processed from 1.0 mm to 0.2 mm using a cold drawing of one stage and two stages. Then the wires of diameter 0.2 mm were annealed at various temperatures in the range of 400-500 oC. The phase t...