Hydrogen accelerated fatigue crack growth of rolled 304L stainless steel
碩士 === 國立臺灣海洋大學 === 材料工程研究所 === 98 === The effects of rolling and sensitization treatment on the hydrogen-assisted fatigue crack growth of 304L stainless steel (SS) were investigated. The results revealed accelerated fatigue crack growth occurred for all the specimens tested in gaseous hydrogen....