Cu3-xMnxAl (x=0.1, 0.2, 0.3, 0.4)合金淬火狀態微結構變化
碩士 === 國立交通大學 === 材料科學與工程系所 === 93 === The as-quenched microstructure of the alloy A (Cu2.9Mn0.1Al) was D03 phase containing plate-like γ1΄ martensite. When the manganese content was added to the 8 at%, the as-quenched microstructures of alloys B (Cu2.8Mn0.2Al) and C (Cu2.7Mn0.3Al) were changed to (...