failure analysis on spent fuel zirconium cladding delayed hydride cracking
碩士 === 國立臺灣科技大學 === 機械工程系 === 91 === The zircaloy delayed hydride cracking is one of the possible degradation mechanisms for spent fuel in interim storage which is also a major factor of causing long axial cracks on cladding and severe fuel failure in the past few years. The ai...