Hydrogen Embrittlement of 17-4 Precipitatipn Hardening Stainless Steel
碩士 === 國立海洋大學 === 材料工程研究所 === 90 === Hydrogen permeation rate and diffusivity in H900 specimen is lower than in SA specimen of 17-4 PH stainless steel. Hydrogen trapped in the interface between copper rich precipitates and matrix and caused brittle fracture in hydrogen environment. Hydrogen diffusio...