Microstructure evolution during extrusion of AA3xxx aluminum alloys
The through process microstructural evolution of aluminum alloys AA3003 (1.27wt% Mn) and AA3102 (0.26wt% Mn) during high temperature extrusion was investigated. The Direct Chill(DC) cast microstructure of both alloys showed interdendritic eutectic regions consisting of rod/plate like constituent pa...