Kinetics of transformation of metastable silver-copper solid solutions

Kinetics of transformation of metastable silver-copper solid solutions

Metastable solid solutions were obtained at compositions across the entire range from 0 at. % Ag;Cu to 100 at. % Ag;Cu by rapid-quenching from the liquid state. Lattice parameters were measured by x-ray diffraction in Debye-Scherrer powder cameras. The enthalpy of solution of the 75.0 at. % Ag;Cu co...

Full description

Bibliographic Details
Main Author: Linde, Ronald Keith
Format: Others
Published: 1964
Online Access:https://thesis.library.caltech.edu/4121/1/Linde_rk_1964.pdf
Linde, Ronald Keith (1964) Kinetics of transformation of metastable silver-copper solid solutions. Dissertation (Ph.D.), California Institute of Technology. doi:10.7907/9F9D-3011. https://resolver.caltech.edu/CaltechETD:etd-10172002-121425 <https://resolver.caltech.edu/CaltechETD:etd-10172002-121425>

Internet

https://thesis.library.caltech.edu/4121/1/Linde_rk_1964.pdf
Linde, Ronald Keith (1964) Kinetics of transformation of metastable silver-copper solid solutions. Dissertation (Ph.D.), California Institute of Technology. doi:10.7907/9F9D-3011. https://resolver.caltech.edu/CaltechETD:etd-10172002-121425 <https://resolver.caltech.edu/CaltechETD:etd-10172002-121425>

Similar Items