Forming pressure effect on microstructure and mechanical properties of nanocrystalline aluminum synthesized by inert gas condensation
The preparation of nanocrystalline aluminum (NC Al) was conducted in two steps. After the NC Al powder was synthesized by an Inert gas condensation (IGC) method in a helium atmosphere of 500 Pa, the NC Al powder was in-situ compacted into a pellet with a 10 mm diameter and 250 μm-300 μm thickness in...