Investigation of Microstructure and Nanoindentation Hardness of C<sup>+</sup> & He<sup>+</sup> Irradiated Nanocrystal SiC Coatings during Annealing and Corrosion
The microstructure and nanoindentation hardness of unirradiated, irradiated, annealed and corroded SiC coatings were characterized. Irradiation of 400 keV C<sup>+</sup> and 200 keV He<sup>+</sup> with approximately 10 dpa did not cause obvious amorphous transformation to nano...