In Situ Formation of TiB2/Al2O3-Reinforced Fe3Al by Combustion Synthesis with Thermite Reduction
Fabrication of Fe3Al–TiB2–Al2O3 composites with a broad range of phase compositions was studied by combustion synthesis involving aluminothermic reduction of oxide precursors. Two reaction systems composed of elemental Fe, amorphous boron, and a thermite mixture of Fe2O3/TiO2/Al were conducted in th...