Hot Corrosion Behavior of Sputtered Nanocrystalline Coating with Yttrium Addition at 900 °C
The high temperature corrosion behavior of sputtered nanocrystalline K38 coating with and without yttrium addition under mixed molten salt film in air was investigated. Accelerated corrosion occurred on the coating without yttrium (Y) addition locally after 60 h exposure at 900 °C, which resulted in...