The Sequence of the Phase Growth during Diffusion in Ti-Based Systems
The interdiffusion in Ti-based alloys was studied. It was shown that during diffusion at 1,123 K formation of four intermetallic phases occurs. The diffusion paths for six different diffusion couples were determined. Moreover, the entropy production was calculated – the approximation used for determ...