Effect of Austenite-to-Ferrite Phase Transformation at Grain Boundaries on PWHT Cracking Susceptibility in CGHAZ of T23 Steel
The post-weld heat treatment (PWHT) cracking susceptibility of a coarse grain heat-affected zone (CGHAZ) in SA213-T23 (2.25Cr-1.6W steel) that was used for boiler tubes employed in thermal power plants was investigated using a Gleeble thermal cycle simulator. The PWHT cracking susceptibility test wa...