Sol-derived Hydroxyapatite Ddip-coating of a Porous Ti6Al4V Powder Compact
A sintered porous Ti6Al4V powder compact with a mean pore size of 63 µm and an average porosity of 37±1% was dip-coated at soaking times varying between 1- and 5-minute using a sol-derived calcium Hydrooxyapatite (HA) powder. The coated compacts were heat-treated at 840 oC. The coating thickness was...