Crack initiation and early propagation behavior of AlSi10Mg(Cu) cast alloy under thermal fatigue
The damage evolution under thermal fatigue loading for AlSi10Mg(Cu) cast alloy on the crack initiation and early propagation stage, mainly focusing on the influence of silicon particles on the thermal fatigue crack behaviour. The results show that, thermal fatigue crack origins from the failure inte...