Corrosion resistance of low SiC particle variation at low weight content on 1060 aluminum matrix composite in sulfate-contaminated seawater
The effect SiC particle sizes (3 µm, 9 µm 29 µm and 45 µm) at 2.5% weight content on the corrosion resistance of 1060 aluminum in sulfate and sulfate-chloride solution was studied by potentiodynamic polarization, open circuit potential measurement and optical microscopy. Results showed the presence...