<sup>1</sup>H NMR Spin-Lattice Relaxometry of Cement Pastes with Polycarboxylate Superplasticizers
<sup>1</sup>H spin-lattice relaxometry (T<sub>1</sub>, longitudinal) of cement pastes with 0 to 0.18 wt % polycarboxylate superplasticizers (PCEs) at intervals of 0.06 wt % from 10 min to 1210 min was investigated. Results showed that the main peak in T<sub>1</sub>...