The Enrichment of (Cu, Sn) Solid Solution Driven by High-Pressure Torsion

The Enrichment of (Cu, Sn) Solid Solution Driven by High-Pressure Torsion

Cu–14 wt% Sn alloy was annealed at temperatures of 320 and 500 °C. The concentration of tin <i>c</i><sub>init</sub> in the copper-based matrix increased with annealing temperature. The annealed samples were subjected to high-pressure torsion (HPT) at 6 GPa, 5 turns, 1 rpa. HP...