Formation of Large Size Precipitate-Free Zones in β Annealing of the Near-β Ti-55531 Titanium Alloy
Large size (>10000 μm<sup>2</sup>) precipitate-free zones in the absence of microsegregation were observed in the near-β Ti-55531 titanium alloy after furnace cooling from high temperature and longtime annealing in the single-β phase field. To reveal the...