Effect of thermal aging conditions on the corrosion properties and hardness of a duplex stainless steel
The corrosion properties of a 22.5 wt. (%) Cr duplex stainless steel were investigated after long-term aging of 3000, 5000 and 7000 hours at 300 and 400 ºC. The corrosion resistance was measured based on mass loss in a FeCl3 10 wt. (%) solution and electrochemical measurements in a 0.1 M H2SO4 solut...