Effects of Grain Boundary Morphologies on Stress Corrosion Cracking of Alloy 600
Effects of grain boundary morphologies on stress corrosion cracking (SCC) of Alloy 600 have been studied in 40% NaOH at 315°C using C-ring specimens. The configuration of the grain boundary and the intergranular carbide density were controlled by heat treatment. SCC tests were performed at +150 mV a...