Effect of cold rolling and annealing temperature to the characteristics of α + β' phases in Cu-29.5Zn-2.5Al alloy produced by gravity casting
Al-brass alloys (Cu29.5Zn2.5Al wt. %) were produced by gravity casting and homogenized at 800°C for 2 h, resulting in a binary phase morphology identified as cubic α and martensitic βʹ phases through X-ray diffraction (XRD). Samples were then subsequently cold rolled and annealed at 150, 300, 400, a...