Microstructure And Texture Evolution During Cold-Rolling In The Fe-23Mn-3Si-3Al Alloy
Fe–23wt.%Mn–3wt.%Si–3wt.%Al alloy was cast, homogenized at 1150ºC, hot-rolled at temperatures between 1200ºC and 900ºC and next cold-rolled from 5% up to 40% reductions in thickness. Microstructure and texture of this alloy, which has a low stacking fault energy, were defined after cold-rolling. Inv...