Effect of solidification parameters on the microstructures of a single crystal Ni-based superalloy AM3
A single crystal Ni-based superalloy AM3 was processed at withdraw rates of 3.5, 10, 50, 100, 200, and 500 μm•s-1, respectively. The as-cast microstructures and solidification segregation ratio were characterized with various withdraw rates. The shape and size of carbide microstructures were determi...