The Effects of T5 and T6 Heat Treatments on Wear Behaviour of AA6063 Alloy
In this study, T5 heat treatment was applied to AA6063 alloy aged at 455 K for 2 hours after extrusion at 686 K. T6 heat treatment was also carried out by ageing at 455 K for 2 hours after solution heat treatment at 794 K for 1 hour. Heat treated T5 and T6 specimens were tested by pin-on-disc type w...