Microstructure characterization and hardness of Al-Cu-Mn eutectic alloy
The composition of Al-Cu-Mn ternary eutectic alloy was chosen to be Al-32.5wt.%Cu-0.6wt.%Mn to the Al2Cu and Al12CuMn2 solid phases within an aluminum matrix (α-Al) from its melt. The Al-32.5wt.%Cu-0.6wt.%Mn alloy was directionally solidifi ed at a constant temperature gradient (G=8.1 K·mm-1) with...