High-Temperature Compressive Properties of TiB-Reinforced Ti Alloy via In Situ Synthesis
In this investigation, in situ synthesis of TiB-reinforced Ti-based alloy was carried out by powder metallurgy. The Ti (TiH2)—Al and B powders were ball milled for 40 h to obtain a mixed powder with a nominal composition of Ti-7Al-0.2B (wt. %) and TiH2-7Al-0.2B (wt. %). After milling the m...