Hot Deformation Behavior of Powder Metallurgy Ti-14Mo-2.1Ta-0.9Nb-7Zr Alloy
The new medical Ti-14Mo-2.1Ta-0.9Nb-7Zr alloy was prepared by powder metallurgy. The high temperature compression behavior and the dynamic recrystallization behavior of the alloy were investigated by hot compression tests. The tests were performed with a Gleeble-1500D simulator at 780-960℃ and stain...