Creep crack growth behavior of P91 steel weldments
The steels operating at elevated temperatures are well known to be exposed to premature failure due to cracking caused by constant thermal stress, i. e. secondary creep process. Therefore, creep crack growth tests were carried out on compact tension specimens machined from P91 weld joint at 600°C to...