Enhancing the Corrosion Resistance Performance of Mg-1.8Zn-1.74Gd-0.5Y-0.4Zr Biomaterial via Solution Treatment Process
Microstructure and corrosion behavior of the solution-treated Mg-1.8Zn-1.74Gd-0.5Y-0.4Zr (wt%) alloy were studied. The results of microstructure indicated that the second phases of as-cast alloy was mainly comprised of Mg<sub>12</sub>Zn(Gd,Y) phase, Mg<sub>3</sub>Zn<sub>...