On the transition of short cracks into long fatigue cracks in reactor pressure vessel steels
Short fatigue cracks, having dimension less than 1 mm, propagate at much faster rates (da/dN) even at lower stress intensity factor range (da/dN) as compared to the threshold stress intensity factor range obtained from long fatigue crack growth studies. These short cracks originate at the sub-grain...