Optimization of Vanadium Content for Achieving Higher Wear Resistance and Hardness in High Cr-V White Cast Irons for Ball Tube Mill Liner Application

Optimization of Vanadium Content for Achieving Higher Wear Resistance and Hardness in High Cr-V White Cast Irons for Ball Tube Mill Liner Application

Show other versions (1)

The liner materials in coal fired tube mills are less promising due to lower combination of abrasion wear resistance, hardness and impact toughness properties, thus giving service life of 25,000 to 35,000 hours. In this study, focus was given to develop a high Cr-V cast iron of high abrasion wear re...

Full description

Bibliographic Details
Main Authors: Dhirendra Kumar, G. Jayaraman, M. Swamy, A. H. V. Pavan, Antony M. C. Harison
Format: Article
Language:English
Published: Gruppo Italiano Frattura 2019-07-01
Series:Frattura ed Integrità Strutturale
Subjects:
High Cr cast iron
High Cr-V cast iron
Abrasion wear
Hardness
Impact strength
Online Access:https://www.fracturae.com/index.php/fis/article/view/2275/2599

Internet

https://www.fracturae.com/index.php/fis/article/view/2275/2599

Similar Items