Enhanced Stretch Formability of AZ31 Magnesium Alloy Thin Sheet by Induced Precompression and Sequent Annealing

Enhanced Stretch Formability of AZ31 Magnesium Alloy Thin Sheet by Induced Precompression and Sequent Annealing

In this study, precompression deformation with a strain level of 5.38% along the transverse direction (TD) at room temperature was conducted on a AZ31 magnesium alloy thin sheet with thickness of 1mm. Then subsequent annealing treatment was carried out at various temperatures (200, 300, 400, and 500...