Effect of molarity of TiO2 seeded-template to the growth of ZnO nanostructures
ZnO nanostructures were deposited by solution-immersion method on TiO2 layers by sol-gel spin-coating technique. Seven layers of TiO2 were coated on glass substrates at different molarities, followed by annealing treatment and solution-immersion process in aqueous solution containing 1:1 ratio of 0....
| Main Authors: | , , , , , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
2015
|
| Subjects: | |
| Online Access: | View Fulltext in Publisher |
| LEADER | 01663nam a2200217Ia 4500 | ||
|---|---|---|---|
| 001 | aDOI: 10.1088-1757-899X-83-1-012006 | ||
| 008 | 220210s2015 CNT 000 0 und d | ||
| 245 | 1 | 0 | |a Effect of molarity of TiO2 seeded-template to the growth of ZnO nanostructures |
| 260 | 0 | |c 2015 | |
| 856 | |z View Fulltext in Publisher |u https://doi.org/10.1088/1757-899X/83/1/012006 | ||
| 520 | 3 | |a ZnO nanostructures were deposited by solution-immersion method on TiO2 layers by sol-gel spin-coating technique. Seven layers of TiO2 were coated on glass substrates at different molarities, followed by annealing treatment and solution-immersion process in aqueous solution containing 1:1 ratio of 0.05 M of zinc nitrate hexahydrate (Zn(NO3)(2 center dot)6H(2)O) and hexamethylenetetramine (HMTA) (C6H12N4). FESEM images confirmed that ZnO nanostructures grown on TiO2 seeded-template are in needle-like shape with smaller tip can be observed. Photoluminescence (PL) spectroscopy showed that as the molarity of TiO2 seeded-template increase, the intensity of PL emission at UV region decrease. UV emission peak for 0.10 M and 0.25 M are higher compared to UV emission peak film of 0.50 M and 1.00 M, which are too low. Meanwhile, the UV absorption properties of the nanostructured thin film for 0.25 M of TiO2 seeded-template was higher compared to other thin films | |
| 650 | 0 | 4 | |a OPTICAL-PROPERTIES |
| 700 | 1 | 0 | |a Aadila, A |e author |
| 700 | 1 | 0 | |a Afaah, AN |e author |
| 700 | 1 | 0 | |a Alrokayan, SAH |e author |
| 700 | 1 | 0 | |a Asib, NAM |e author |
| 700 | 1 | 0 | |a Khan, HA |e author |
| 700 | 1 | 0 | |a Khusaimi, Z |e author |
| 700 | 1 | 0 | |a Lim, YC |e author |
| 700 | 1 | 0 | |a Mahmud, MR |e author |
| 700 | 1 | 0 | |a Rusop, M |e author |