| Summary: | Regenerated fibers can be prepared from a cooled solution of renneted casein micelles in a wet spinning process. For better handling and stability of the fiber, plasticizers, network modifiers or cross-linkers are used in the production process. For that reason, fibers with different glycerol and calcium content are prepared in this study and subsequently treated with the enzyme transglutaminase before being characterized after air drying. In addition to the swelling behavior in NaOH, H2O, simulated milk ultrafiltrate buffer as well as HCl, the mechanical properties of the fibers are investigated, taking into account their microscopic fine structure. Transglutaminase-treated fibers show sigmoidal absorption curves for all solvents and reach higher equilibrium swelling percentages than untreated fibers. When the calcium content in the coagulation bath is increased from 50 mM to 100 mM, more stabilizing calcium bridges lead to a denser fiber structure that swells more slowly in all solvents considered. With increasing glycerol content, the flexibility of the fibers increases, as indicated by the decrease in elastic moduli, and a fine structure in the sub-µm range becomes visible. The fibers also demonstrate lower elastic moduli when post-treated with transglutaminase. Besides the higher casein content due to the transglutaminase treatment, this could also contribute to the higher equilibrium swelling percentages compared to the untreated fibers. © 2022 by the authors. Licensee MDPI, Basel, Switzerland.
|
|---|