Experiment on Strength and Failure Behavior of Sandstone Containing Pre-Existing Cracks Under Brazilian Compression

Experiment on Strength and Failure Behavior of Sandstone Containing Pre-Existing Cracks Under Brazilian Compression

Determination of the mechanical properties of rock containing pre-existing cracks under tension condition is of great significance to understand the failure process of rock in engineering. This paper presents the experimental results of sandstone containing pre-existing cracks under Brazilian compre...

Full description

Bibliographic Details
Main Authors:	Cao, X. (Author), Qing, Y. (Author), Yu, J. (Author), Yu, T. (Author), Zhang, H. (Author)
Format:	Article
Language:	English
Published:	Frontiers Media S.A. 2021
Subjects:	Brazilian test failure behavior mechanical properties pre-existing crack strength
Online Access:	View Fulltext in Publisher

Similar Items

Effects of pre-existing cracks and infillings on strength of natural rocks – Cases of sandstone, argillite and basalt
by: Chen Cui, et al.
Published: (2020-12-01)

Damage and failure characteristics of rock similar materials with pre-existing cracks
by: Xiaoyu Cheng
Published: (2019-07-01)

Fracture behaviors of pre-cracked monolayer molybdenum disulfide: A molecular dynamics study
by: Qi-lin Xiong, et al.
Published: (2016-10-01)

CRACK STRENGTH OF HOLLOW CORE SLABS: EXPERIMENTAL RESEARCH
by: V. M. Mitasov, et al.
Published: (2019-07-01)

On the crack propagation analysis of rock like Brazilian disc specimens containing cracks under compressive line loading
by: Hadi Haeri, et al.

Effect of loading direction on interaction of two pre-existing open and closed flaws in a rock-like brittle material
by: Mahtab Alitalesh, et al.
Published: (2020-09-01)

A method to model the effect of pre-existing cracks on P-wave velocity in rocks
by: Haimeng Shen, et al.
Published: (2020-06-01)

Failure in Confined Brazilian Tests on Sandstone
by: Tyler Hagengruber, et al.
Published: (2021-03-01)

Experimental study on failure characteristics of jointed rock mass under staged unloading conditions
by: Ping Cao, et al.
Published: (2019-06-01)

The Impacts of Bedding Strength Parameters on the Micro-Cracking Morphology in Laminated Shale under Uniaxial Compression
by: Fakai Dou, et al.
Published: (2020-08-01)

Analysis of Ultimate Compressive Strength of Cracked Plates with the Use of DoE Techniques
by: Woloszyk Krzysztof, et al.
Published: (2020-09-01)

The centrally cracked Brazilian disc: implications and solutions in case of closing cracks
by: Markides Christos F., et al.
Published: (2014-08-01)

Numerical Simulation of the Effect of Loading Angle on Initial Cracks Position Point: Application to the Brazilian Test
by: Meriem Fakhreddine Bouali, et al.
Published: (2021-04-01)

AN INVESTIGATION ON THE EFFECTS OF MICRO-PARAMETERS ON THE STRENGTH PROPERTIES OF ROCK
by: Behzad Jafari Mohammadabadi, et al.
Published: (2021-01-01)

Residual Ultimate Strength of Box Girders with Variable Cracks
by: Lei Ao, et al.
Published: (2015-06-01)

Assessment of residual ultimate strength of cracked plates under biaxial compression
by: LU Yabing, et al.
Published: (2017-10-01)

HYBRID CONTINUUM-DISCONTINUUM MODELLING OF ROCK FRACUTRE PROCESS IN BRAZILIAN TENSILE STRENGTH TEST
by: Huaming An, et al.
Published: (2017-10-01)

Numerical Investigation on Crack Propagation for a Central Cracked Brazilian Disk Concerning Friction
by: Jiuzhou Huang, et al.
Published: (2021-03-01)

Predictive model for the prevention of weld metal hydrogen cracking in high-strength multipass welds
by: Nevasmaa, P. (Pekka)
Published: (2003)

Anisotropy of crack initiation strength and damage strength of coal reservoirs
by: Xianjie HAO, et al.
Published: (2021-02-01)

Behavior and failure mode of reinforced concrete members damaged by pre-cracking
by: Amorn Pimanmas
Published: (2007-07-01)

Restrained Shrinkage Cracking of Fiber-Reinforced High-Strength Concrete
by: Ashkan Saradar, et al.
Published: (2018-02-01)

Experimental Investigation on Crack Behavior and Stress Thresholds of Sandstone Containing a Square Inclusion under Uniaxial Compression
by: Quanqi Zhu, et al.
Published: (2020-10-01)

The failure criterion based on hydrogen distribution ahead of the fatigue crack tip
by: Yu. G. Matvienko
Published: (2013-04-01)

Crack Initiation and Propagation Fatigue Life of Ultra High-Strength Steel Butt Joints
by: Markus J. Ottersböck, et al.
Published: (2019-10-01)

Crack Initiation, Propagation, and Coalescence Experiments in Sandstone Brazilian Disks Containing Pre-Existing Flaws
by: Shijun Zhao, et al.
Published: (2019-01-01)

Experimental Study on Compression Failure of Composite Laminates with Prefabricated Surface Cracks
by: Wei Sun, et al.
Published: (2021-06-01)

MECHANICAL PROPERTIES OF MRP LIGHTWEIGHT CONCRETE AND EFFECT OF COMPRESSIVE STRENGTH ON SHEAR CAPACITY OF BEAMS
by: Wissam Kadhim AlsaraJ, et al.
Published: (2019-09-01)

Experimental Study on Fatigue Crack Propagation of High-Strength Steel Wire with Initial Defects for Bridge Cables
by: Ying Wang, et al.
Published: (2020-06-01)

CURRENT COGNITION OF ROCK TENSILE STRENGTH TESTING BY BRAZILIAN TEST
by: Zlatko Briševac, et al.
Published: (2015-12-01)

Impact of Pre-Existing Immunity to Influenza on Live-Attenuated Influenza Vaccine (LAIV) Immunogenicity
by: Sreeja Roy, et al.
Published: (2020-11-01)

On the decay of strength in Guilin red clay with cracks
by: Yi Li, et al.
Published: (2015-10-01)

Experimental Study on the Shrinkage Properties and Cracking Potential of High Strength Concrete Containing Industrial By-Products for Nuclear Power Plant Concrete
by: Baek-Joong Kim, et al.
Published: (2017-02-01)

Acoustic Emission Multi-Parameter Analysis of Dry and Saturated Sandstone with Cracks under Uniaxial Compression
by: Hongru Li, et al.
Published: (2019-05-01)

Algorithm for automatic fatigue crack growth simulation on welded high strength steels
by: Ricardo Miguel Gomes Simões Baptista, et al.
Published: (2019-03-01)

Algorithm for automatic fatigue crack growth simulation on welded high strength steels
by: R. Baptista, et al.
Published: (2019-04-01)

Effect of Prestrain on Fatigue Crack Growth in Low-carbon Steel
by: Melnikov B.E., et al.
Published: (2011-05-01)

Effective Depletion of Pre-existing Anti-AAV Antibodies Requires Broad Immune Targeting
by: Victoria M. Velazquez, et al.
Published: (2017-03-01)

Experimental Investigation on the Force-Crack Quantification Model for HSRC Columns with Flexure–Shear and Shear Failure Modes
by: Cien-Kuo Chiu, et al.
Published: (2020-06-01)

Hydrogen-assisted stress corrosion cracking of high strength steel
by: Ghasemi, Rohollah
Published: (2011)

Cannot write session to /tmp/vufind_sessions/sess_usfi5hti89iuu1c10qd6t1s2vd