| Summary: | This thesis was carried out in the context of a co-tutoring program between Centro Ceramico Bologna (Italy) and Instituto di Tecnologia Ceramica, Castellón de la Plana (Spain). The subject of the thesis is the synthesis of silver nanoparticles and at their likely decorative application in the productive process of porcelain ceramic tiles.
Silver nanoparticles were chosen as a case study, because metal nanoparticles are thermally stable, and they have non-linear optical properties when nano-structured, and therefore they develop saturated colours. The nanoparticles were synthesized by chemical reduction in aqueous solution, a method chosen because of its reduced working steps and energy costs. Besides such a synthesis method uses non-expensive and non-toxic raw material. By adopting this synthesis technique, it was also possible to control the dimension and the final shape of the nanoparticles.
Several syntheses were carried out during the research work, modifying the molecular weight of the reducing agent and/or the firing temperature, in order to evaluate the influence such parameters have on the Ag-nanoparticles formation. The syntheses were monitored with the use of UV-Vis spectroscopy and the average dimension as well as the morphology of the nanoparticles was analysed by SEM. From the spectroscopic data obtained from each synthesis, a kinetic study was completed, relating the progress of the reaction to the two variables (ie temperature and molecular weight of the reducing agent). The aim was finding equations that allow the establishing of a relationship between the operating conditions during the synthesis and the characteristics of the final product.
The next step was finding the best method of synthesis for the decorative application. For such a purpose the amount of nanoparticles, their average particle size, the shape and the agglomeration are considered.
An aqueous suspension containing the nanoparticles is then sprayed over the fired ceramic tiles and they are subsequently thermally treated in conditions similar to the industrial one. The colorimetric parameters of the obtained ceramic tiles were studied and the method proved successful, giving the ceramic tiles stable and intense colours.
|
|---|