Thermoluminescence of annealed synthetic quartz

• Main Author: Atang, Elizabeth Fende Midiki
• Format: Others
• Language: English
• Published: Rhodes University 2016
• Online Access: http://hdl.handle.net/10962/420

The kinetic and dosimetric features of the main thermoluminescent peak of synthetic quartz have been investigated in quartz ordinarily annealed at 500_C as well as quartz annealed at 500_C for 10 minutes. The main peak is found at 78 _C for the samples annealed at 500_C for 10 minutes irradiated to 10 Gy and heated at 1.0 _C/s. For the samples ordinarily annealed at 500_C the main peak is found at 106 _C after the sample has been irradiated to 30 Gy and heated at 5.0 _C/s. In these samples, the intensity of the main peak is enhanced with repetitive measurement whereas its maximum temperature is unaffected. The peak position of the main peak in the sample is independent of the irradiation dose and this, together with its fading characteristics, are consistent with first-order kinetics. For doses between 5 and 25 Gy, the dose response of the main peak of the annealed sample is superlinear. The half-life of the main TL peak of the annealed sample is about 1 h. The activation energy E of the main peak is around 0.90 eV. For a heating rate of 0.4 _C/s, its order of kinetics b derived from the whole curve method of analysis is 1.0. Following irradiation, preheating and illumination with 470 nm blue light, the main peak in the annealed sample is regenerated during heating. The resulting phototransferred peak occurs at the same temperature as the original peak and has similar kinetic and dosimetric features, with a half-life of about 1 h. For a preheat temperature of 200 _C, the intensity of the phototransferred peak in the sample increases with illumination time up to a maximum and decreases thereafter. At longer illumination times, no further decrease in the intensity of the phototransferred peak is observed. The traps associated with the 325 _C peak are the main source of the electrons responsible for the regenerated peak.