| Summary: | This research project was conducted to increase weld gap tolerance in Friction Stir Welding (FSW) of 8 mm thick aluminum alloy 6082 – T6. Investigation was done on I-STIR PDS platform and a Johnford milling machine. The research project involved tool-pin design with varying re-entrant features and varying parameters as a method of weld gap closing to produce successful welds. Direction of spindle rotation and dwell time were established as part of a preliminary study. Clockwise spindle rotation with 20 seconds dwell time allows sufficient plasticity and improved material flow which assisted in achieving welds with prior 30 percent weld gap of the plate thickness. Final welds were made using three rotational speeds and feed rates with sufficient plunging to prevent root defects. Analysis of the results were detailed which include vickers microhardness test, tensile test and metallographic observation to access the suitability of the weld structure. From the set of tool-pins designed, the flare tool-pin gave a well-defined weld nugget with improved stirring at the weld root. Also, with a concave shoulder, right hand threaded tool-pin and counterclockwise flutes undergoing a clockwise spindle rotation, plasticized material flow was upward which was beneficial in reducing the amount of plate thinning. The right hand thread counter clockwise flute with a flute machined in the foot exhibited superior tensile strength for welds containing 30 percent weld gap.
|
|---|